PETG Specialty Model Material for MakerBot Method

As low as $69.00

 

Do you need help choosing the right 3D Printer for your application or require a quote to purchase?

Contact MakerBot

PETG SPECIALTY MATERIAL

PETG is the material of choice for printing high-performance parts that demand excellent durability along with temperature, moisture, and chemical resistance. Engineers and designers use PETG to produce durable prints with speed and agility that can withstand industrial applications including functional prototypes, jigs and fixtures, and end-use parts.

WHAT'S INCLUDED:

1 Spool of PETG Specialty Model Material

PRINTER COMPATIBILITY
MakerBot Method

SPOOL TYPE
Smart Spool™ provides valuable information including material type, color, and amount remaining via an RFID chip directly to MakerBot Print, while a desiccant in the spool maintains a low moisture level inside the drawer bay.

SPECIALTY MATERIAL USER NOTE
Specialty Materials provide basic print performance and can require additional workflow steps to print successfully. PETG requires the application of adhesion stick to the build plate prior to printing.

MATERIAL DATA
Moisture Resistance (ISO 62): 1104 ppm
Heat Deflection - ASTM 648: 70°C (158°F)
Flexural Strength (ISO 178): 69 MPa (10007 psi)
Flexural Modulus (ISO 178): 2050 Mpa (297,327 psi)
Tensile Strength at yield (ISO 527): 50 Mpa (7251 psi)
Tensile Modulus (ISO 527): 2020 MPa (292976 psi)
Strain at Yield - Elongation (%): 6%
Impact Strength (Charpy method 23C): 8.1 kJ/m2 (3.85 ft-lb/in2)

 

DIMENSIONS AND WEIGHT
Spool Diameter: 21.8 cm (8.6 in)
Spool Width: 4.2 cm (1.65 in)
Material Diameter: 1.75 mm
Shipping Weight: 1.1 kg (2.4 lb)
Net Weight: 0.75 kg (1.65 lb)

STORAGE ENVIRONMENT
Store in the included a vacuum-sealed metalized polyester bag to avoid moisture absorption from air; long-term exposure to humidity can compromise material quality and performance. Make sure the built-in desiccant is in the spool to absorb any moisture exposure during the material loading process.